Numerical simulation of stress and deformation of in-service welding onto gas pipeline

SYSWELD was used to simulate in-service welding process of gas pipeline of X70 pipeline steel. Welding thermal cycle, stress and deformation of in-service welded joint were studied. The results show that peak temperature of coarse grain heat-affected zone (CGHAZ) of in-service welding onto gas pipeline is the same with routine welding, but t8/5 ,t8/3 and t8/1 decrease at certain degree. For the zone near welded seam, axial stress and hoop stress in the inner pipe wall are compressive stress when welding source passes through the cross-section that is studied, but residual axial stress and residual hoop stress after welded are all tensile stress. Transient deformation and residual deformation are all convex deformation compared with the original pipe diameter size. Deformation achieves maximum when welding thermal source passes through the cross-section that is studied and then decreases during the cooling process after welding.