Preparation of doping titania antibacterial powder by ultrasonic spray pyrolysis

Doping titania powders were synthesized by ultrasonic spray pyrolysis method from an aqueous solution containing H2TiF6 and AgNO3. The effects of the processing parameters on panicle size distribution, structure, and morphology of doping panicles were investigated. The results show that aggregation-free spherical panicles with average diameter of 200-600 nm are obtained and the particle size of the powder can be controlled by adjusting the concentration of solution. The experimental approach indicates that the size and the value of standard deviation of panicle size increase from 210 nm to 450 nm and from 0.46 to 0.73 respectively with the increase of the titanic ion concentration from 0.05 to 0.4 mol/L. Composite TiOF2 is obtained when the pyrolysis temperature is set to be 400 ℃. With increasing pyrolysis temperature from 400 ℃ to 800 ℃, the crystal size of titania powders increases from 14.1 to 26.5 nm and TiOF2 content of powder decreases dramatically. The property of ion released from powder is affected significantly by the pyrolysis temperature, and the amount of fluorine ion and silver ion released from powder decrease with increasing pyrolysis temperature. The optical property of doping titania powders is not affected by pyrolysis temperature. Antibacterial test results show that composite powders containing more fluorine ions exhibit stronger antibacterial activity against E.coli.