Effects of Doping CeO2, Er2O3 on Properties of TiO2-SiO2 Ceramics for Catalyst Supporter of deNOx

Effects of doping CeO2 and Er2O3 on the mechanical strength, thermal expansion coefficient, sintering temperature of TiO2-SiO2 ceramics were investigated. The experimental results and the microscopic analysis of SEM, XRD, TG-DSC, FT-IR and TEM show that adding CeO2 and Er2O3 into TiO2-SiO2 ceramics can prohibit the growth of its crystal grains, make their size uniform and form them into a dense structure, which finally enhance its mechanical behaviors, and the lower thermal expansion coefficient that leads to an excellent property of thermal shock resistance. After the reforming TiO2-SiO2 ceramics doped by CeO2 was sintered at 1380 ℃, the bending strength reached to 83 MPa, and the thermal expansion coefficient was 9.8×10-6/℃ within the temperature range of 25～800 ℃, which provides a promising basis of making equipped honeycomb catalyst of deNOx.