管道三层结构聚烯烃防腐蚀技术及应用现状

第23卷第5期腐蚀与防护VoL. 23 No 52002年5月corrosion PROtECTIONMay 2002管道三层结构聚烯烃防腐蚀技术及应用现状杨晓鸿(武汉工业学院生化系,武汉430023)摘要:介绍了管道三层结构聚烯烃外防护技术的基本特点和技术要求,以及该技术在目前的应用情况气管道对耐蚀材料的需求量巨大,开发配套的粉末涂料和性能更好的改性聚烯烃树脂,是涂料市场新的增长点。关键词:三层结构聚烯烃;粉末涂料;防腐蚀中图分类号:TE988.2文献标识码:A文章编号:1005748X(2002)05020204APPLICATION OF 3-LAYER POLYETHYLENE ANTICORROSIONSYSTEM FOR PIPELINEYANG Xiao-hong(Biochemistry Dept. of wuhan Polytechnic Univ, Wuhan 430023, China)Abstract: In this paper, the fundamental characteristics, technique requirements and application of 3-layerpolyethylene anticorrosion system for pipelines are presented. Since the pipeline construction in China needs a largenumber of anticorrosion materials, the development of fusion bonded epoxy powder coating and better polyethyleneresin should be a new increasing site in the coating marketKey words: 3-Layer polyethylene system: Powder coating: Anticorrosion1引言能,使之成为目前世界上最先进的管道外防腐涂层结构,已在国内外大量推广开来。本文就管道三层随着“西气东输”工程的实施启动,开始大规模结构聚烯烃防腐技术及其应用现状作一介绍。建设长距离天然气长输管道,这极大促进了管道防腐层材料市场和技术的发展成为目前产业和学术2三层结构聚烯烃防腐技术界关注的热点2.1三层结构聚烯烃防腐层简介天然气长输管道属埋地的隐蔽工程,管道防腐聚乙烯防腐层分两层结构和三层结构两种。两层技术的采用和施工质量直接关系到管道的安全运层结构的底层为胶粘剂,外层为聚乙烯;三层结构的行和使用寿命。随着管道建设向沙漠、沼泽冻土和底层为环氧涂料中间层为胶粘剂,面层为聚烯烃海洋等苛刻环境的延伸以及输送介质的多样化,要三层结构中的环氧涂料可以是液体环氧涂料,也可求防腐层能够满足更加苛刻的环境和工艺条件,并以是环氧粉末涂料。图1是管道三层复合外防腐涂且有更长的使用年限。近年来,国内外在管道防腐层结构图层材料和技术方面都取得了快速进步,新材料、新工三结构骤稀记艺和新设备不断出现。前用于埋地管道外防腐的材料和技术主要有:石油沥青防腐层技术、煤焦油瓷漆防腐层技术环氧涂料防腐层技术、聚乙烯胶粘带防腐层技术、熔钢管粉末胶粘层聚稀结环氧粉末防腐层技术、二层结构聚乙烯防腐层、三层结构聚烯烃防腐层技术等。其中三层结构聚烯烃图1管道三层结构聚烯烃防腐涂层防腐层集成了溶结环氧粉末涂层优异的耐化学介质2.2结构及等级性能和聚烯烃涂层极佳的耐水气渗透和机械保护性采用聚乙烯层外防腐技术时,应根据不同的土中国煤化工的防腐层。不同直收稿日期:200201-12乙烯防腐层厚度见表CNMHG202杨晓鸿:管道三层结构聚烯烃防腐蚀技术及应用现状1,焊缝部位的防腐层厚度不宜小于表中规定值的表5聚乙烯混合料的压制片材性能指标90%性能指标试验方法表1聚乙烯防腐层的厚度1拉伸强度/MPa≥20GB/T1040-1992钢管公称直径环氧涂料层胶粘剂层外防护层最小厚度/mm2断裂伸长率/%≥600GBT1040-1992dN/ mn普通型加强型3维卡软化点/℃B/T1633-19794脆化温度/℃C≤-65GB/T5470-19855电气强度/Mv·m≥25GB/T1408-19896体积电阻率/n·m≥1×103GB/T1410-198250