Effect of hot rolling on the microstructure and impact absorbed energy of the strip steel by CSP

The microstructures and impact absorbed energies at various temperatures were investigated for steel strips hot rolled to thickness reductions of 95.5%, 96.0%, 96.5%, 97.0%, and 97.5%. Results indicate that grain refinement can be realized with an increase in hot rolling reduction. Besides, finer precipitates can be achieved with an increase in hot rolling reduction from 95.5%to 97.0%. The impact absorbed energy decreases with a decrease in testing temperature for steel strips hot rolled to 95.5%, 96.0%, and 96.5%reductions in thickness. How-ever, in the case of steel strips hot rolled to 97.0%and 97.5%reductions in thickness, the impact absorbed energy remained almost constant with a decrease in testing temperature.