Preparation of Nano-Particles (Pb,La)TiO3 Thin Films by Liquid Source Misted Chemical Deposition

Nano-particles lanthanum-modified lead titanate (PLT) thin films are grown on Pt/Ti/SiO2/Si substrate by liquid source misted chemical deposition (LSMCD). PLT films are deposited for 4-8 times, and then annealed at various temperature. XRD and SEM show that the prepared films have good crystallization behavior and perovskite structure. The crystallite is about 60 nm. The deposition speed is 3 nm/min. This deposition method can exactly control stoichiometry ratios, doping concentration ratio and thickness of PLT thin films. The best annealing process is to bake at 300 ℃ for 10 min and anneal at 600 ℃ for 1 h.