贫瘦煤配煤炼焦研究

2009年6 月武钢技术Jun, 2009第47卷第3期WISCO TECHNOLOGYVol.47 No.3 ●11●贫瘦煤配煤炼焦研究张雪红,薛改凤,陈鹏,项茹,张前香(武钢研究院,湖北武汉430080)摘要: 对贫瘦煤参与配煤的问题进行研究，通过对不同粒度贫瘦煤参与配煤炼焦所得坩埚焦热性能、结构强度、显微强度、成焦结构的分析,得出贫瘦煤的细粉碎有利于焦炭质量的提高,同时得出细粉碎的最佳粒度。关键词:贫瘦煤;配煤;炼焦;细粉碎中图分类号: TQ520.62文献标识码: A文章编号: 1008-4371(2009)03-0011-03Research on meagre-lean coal used in coal blending and coke -makingZHANG Xue hong,XUE Gai-feng,CHEN Peng, XIANG Ru,Zhang Qian: xiang(Research and Development Center, Wuhan Iron and Steel Corp ,Wuhan 430080, China)Abstract: Usage of meager-lean coal in coal blending is studied. By analysis on the tech-nological parameters such as the thermal properties, structural strength, micro strengthand microstructure of crucible coke acquired in the process of coal blending and cokemaking with different grain sizes of the meager coal it's concluded that fine grinding ofmeager coal is good to the improvement of coke quality and the optimal grain size of finegrinding is determined as well.Key words:meager coal;coal blending; coking;fine grinding随着高炉大型化对焦炭质量要求的提高及炼1 实验研究焦配煤成本降低的需求,贫瘦煤由于其资源相对较广、价格便宜引起焦炭生产厂家的注意。贫瘦实验用煤样灰分9. 58 %,挥发分15.68 %,G煤具有变质程度高它具有变质程度高、挥发分低值为18。煤样首先进行缩分，以保证煤样的均匀和粘结性差等特点。其单独炼焦时,由于机械强性,然后对煤样进行细粉碎,控制其最大粒度分别度差,所得焦炭块度较大,由于机械强度差。但贫为a mm、b mm、c mm.d mm,e mm。瘦煤存在高变质程度.弱粘结性等缺点,若仍按旧坩埚焦的制备,称量600 g煤样置于刚玉坩的配煤理论和配煤技术条件,将贫瘦煤用于配煤埚中,加热至950C。焦炭结构强度参照原苏联炼焦,势必将影响焦炭质量。邯钢、马钢等厂家已rOCT9521标准。显微强度参照华东冶金学院安根据自己的配煤资源特点配人4 %~5 %的贫瘦徽工业大学规程,焦样改为5 g,钢球改为15个。煤,在保证焦炭质量的前提下,降低了配煤成焦炭的热性能测定参照GB/T4000- 1996 试验本[1-2]。本文采用贫瘦煤自身细粉碎的粒度变化条件,反应时间为1h。焦炭的显微组成(即光学进行配煤炼焦研究,以期在现有的条件下,扩大炼组织) ,是将不同粒度贫瘦煤参与配煤所得焦块焦煤资源,缓解煤资源的供需矛盾,保证焦炭质制取焦样,按YB/T 077- 1995规程采用数点统量.降低配煤成本.提高企业竞争力。同时现有瘦计法,在德国进口的MSP- 200 显微光度计上进煤资源存在变质程度升高,日渐走向贫瘦化的趋行测定。势,也要求配煤炼焦研究人员探讨相适应的配煤中国煤化工理论。MYHCNMHG作者简介:张雪红(1979-).女,硕士,助理工程师●12●武钢技术第47卷885t2实验结果 与分析87--5486-2.1 不同粒度的贫瘦煤参与配煤炼焦8552_实验固定配煤比(其中贫瘦煤为25 %),贫瘦B 84煤细粉碎按表1中的粒度要求控制(a>b>c>d83-> >e) ,并进行坩埚焦配煤炼焦试验。82+ MSI4681J44表1不同粒度贫瘦煤参 与配煤方案