Failure analysis used for remanufacturing of steel rolling components

The guide-pieces, used in the process line of steel roiling, were the important components. The guidepieces, which were slide contacting with the rolled-piece, had a high temperature and high speed. The wear was very serious. The results from failure analysis showed that there were three failure forms in the guide-pieces: the first was the wear during heat friction, the second was the heat fatigue under the cycle of deep heating and deep cooling, and the third was the impact rupture. Among them, the wear was the main reason. To the wear of guidepieces, there were four mechanisms, namely abrasive wear, adhesive wear, fatigue wear and corrosion wear. The failure analysis to the guide-piece laid the foundation for its remanufacturing.