Influence of Yttrium Ion-implantation on Oxidation Kinetics of Co-40Cr Alloy and Property of Oxide/S

The isothermal and cyclic oxidizing kinetics of Co-40Cr alloy and its yttrium ion-implanted samples were studied at 1000℃ in air by thermal-gravity analysis (TGA). Scanning electronic microscopy (SEM) was used to examine the Cr2O3 oxide film's morphology after oxidation. Secondary ion mass spectroscopy (SIMS) method was used to examine the binding energy change of chromium caused by yttrium doping. Acoustic emission (AE) method was used in situ to monitor the cracking and spalling of oxide films formed on both samples during oxidizing and subsequent air-cooling stages. It is found that yttrium implantation remarkably reduces the isothermal oxidizing rate of Co-40Cr and improves the anti-cracking and anti-spalling properties of Cr2O3 oxide film. The reasons for the improvements are mainly that implanted yttrium reduces the grain size of Cr2O3 oxide, increases the high temperature plasticity of oxide film, and remarkably reduces the number and size of Cr2O3/Co-40Cr interfacial defects.